K-TiC based cemented carbide inserts | K-TiC Cermet Inserts

K-TiC based cemented carbide inserts
K-TiC based cemented carbide inserts
K-TiC based cemented carbide inserts
K-TiC based cemented carbide inserts

Hunan Kingcera Engineering Co., Ltd. combined production technology of powder metallurgy and wear resistant ceramic, K-TiC cermet inserts is an upgraded one in similar product market. Aiming to provide better and more reliable cermet composite solution for all kinds high manganese or low alloy wear parts ‘wear resistance performance in the field of mining,cement, steel making.

Brand:KINGCERA

Origin:Changsha China

Categories:TiC Cermet Inserts

Follows:

PRODUCT DETAILS

Product Introduction

Hunan Kingcera Engineering Co., Ltd. combined production technology of powder metallurgy and wear resistant ceramic, K-TiC cermet inserts is an upgraded one in similar product market. Aiming to provide better and more reliable cermet composite solution for all kinds high manganese or low alloy wear parts ‘wear resistance performance in the field of mining,cement, steel making. 
 
For K-TiC cermet inserts, common grade details as below
Grade Composition Details Application
TM52 Titanium carbide 48%,
high manganese steel and others 52%
High abrasion resistance and high toughness, widely used in crushers’ wear part by casting
TM60 Titanium carbide 40%,
high manganese steel and others 60%
Compared to TM52, higher toughness, but lower abrasion resistance, usually used in  road header, shaft drilling machine;
GT35 Titanium carbide 35%,
high manganese steel and others 65%
Ultra high toughness, usually for mold making
 
In current stage, Grade TM52 is the hot sale and widely used one in casting field.
 
Grade TM52 Technical data
Item Value Range Testing Standard or Equipment
Density g/cm³ 6.0-6.2 ISO3369 OR GB/T3850
Hardness HRC - 60-62 ISO3781 ORGB/T3849
Bending Strength MPa ≥1600 ISO3327 OR GB/T3851
Impact  J/mm² ≥6.0 GB/T1817
Porosity - A02B00C00 ISO4505 OR GB/T3489
Size   As request  

Hot sale size in cylinder shape:  D12x50mm, D14x60mm,D14x40mm,D14x50mm,D16x80mm,D18x80mm, D20x90mm;
Tailored size: as request, could make;
Free Sample: as request.
 

Why K-TiC cermet inserts in Hunan Kingcera is an upgraded one in similar product market?

Item One:After ordinary dry press process, add cold isostatic pressing(CIP), which we used for wear resistant ceramic products almost 30years. After two step pressing, pre-sintering rods will get higher compactness, which will bring evenly shrinkage during sintering, then get compacted K-TiC cermet rods. 
Item Two: for pre-sintering inserts, could use wire cutting process to make tailored shape & size 
Item Three:Use vacuum sintering process. The surface of inserts appears own bright silver metal luster by visual testing, which means the inserts be fully sintered, all above mentioned technical performance will be guaranteed.
Item Four:self-design and produce ability in mold making, could make tailored inserts, right now, biggest rod size is D20x110mm
Item Five:all production processes are under control of ISO14001:2015.

Product Applications

Each batcApplication products: high manganese wear parts, hammer crusher, hammer head, plate hammer, movable jaw plate, tooth plate, cone crushing wall, rolling mortar wall, crushing cavity, fixed cone liner, movable cone liner, roller ring of roller machine, cone crushers, Metso HP series cone crusher 
Applicable crushing equipment: jaw crusher, single-stage hammer crusher, ring hammer crusher, impact crusher, cone crusher, gyratory crusher, plate feeder, counter-roller;
Applied material: high manganese steel, manganese chromium alloy (Mn13, Mn13Cr2, Mn18, Mn18Cr2), low alloy steel
Application casting process: V method, lost foam, sand casting
Application materials: large ore, iron ore, gold ore, copper ore, river pebble, granite, basalt, iron ore, limestone, quartzite, diabase, etc.
Application range: ore crushing, limestone mines, sand and gravel yard, concrete mixing plant, dry mortar, power plant desulfurization, quartz sand, etc.
Application industries: ore mining industry, cement industry, building materials industry, etc.h will take hardness testing by professional equipment.